Role of stoichiometric and nonstoichiometric defects on the magnetic properties of the half-metallic ferromagnet NiMnSb [Elektronisk resurs]
-
Alling, Björn 1980- (författare)
-
Shallcross, Sam 2000- (författare)
-
Abrikosov, Igor 1965- (författare)
-
- Linköpings universitet Institutionen för fysik, kemi och biologi (utgivare)
-
-
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik
(tidigare namn)
-
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik, biologi och kemi
(tidigare namn)
-
Alternativt namn: IFM
-
Alternativt namn: Engelska : Department of Physics and Measurement Technology, Biology and Chemistry
-
Alternativt namn: Engelska : Department of Physics, Chemistry and Biology
-
- Linköpings universitet Tekniska högskolan (utgivare)
-
-
Alternativt namn: Linköpings universitet. Tekniska fakulteten
-
Alternativt namn: Linköpings tekniska högskola
-
Alternativt namn: Tekniska högskolan vid Linköpings universtiet
-
Alternativt namn: LiTH
-
Alternativt namn: Linköping University. Institute of Technology
-
Se även: Universitet i Linköping Tekniska högskolan
- 2006
- Engelska.
-
Ingår i: Physical Review B. Condensed Matter and Materials Physics. - 1098-0121. ; 73:6, 064418
-
Läs hela texten
-
Läs hela texten
-
Läs hela texten
Sammanfattning
Ämnesord
Stäng
- The first material to be predicted from first-principles calculations as half-metallic was NiMnSb, and the research on this material has been intense due to its possible applications in spintronics devices. The failure of many experiments to measure spin polarization to more than a fraction of the predicted 100% has partly been blamed on structural defects. In this work a complete first-principles treatise of point defects, including nonstoichiometric antisites, interstitial and vacancy defects, as well as stoichiometric atomic swap defects in NiMnSb, is presented. We find that the formation energies of the defects span a large scale from 0.2 to 14.4 eV. The defects with low formation energies preserve the half-metallic character of the material. We also find that some of the defects increase the magnetic moment and thus can explain the experimentally observed increase of magnetic moments in some samples of NiMnSb. Most interesting in this respect are Mn interstitials which increase the magnetic moment, have a low formation energy, and keep the half-metallic character of the material.
Ämnesord
- Natural Sciences (hsv)
- Naturvetenskap (hsv)
- NATURAL SCIENCES (svep)
- NATURVETENSKAP (svep)
Indexterm och SAB-rubrik
- nickel alloys
- manganese alloys
- antimony alloys
- ferromagnetic materials
- ab initio calculations
- interstitials
- antisite defects
- vacancies (crystal)
- defect states
- magnetic moments